What Is The Hardness Of Conventional Silicone

The hardness of conventional silicone is generally between 10A-70A .In addition, when the hardness is between 20 and 40 degrees, the tear strength, elongation, etc. are optimal. When the hardness of silicone is lower than 10 degrees, the tear strength of the silicone is low, the elongation is large, and the silicone products are easily deformed; when the hardness is higher than 40 degrees, the tear strength becomes poor, and the silicone products become brittle and easy to break .

1. Measurement method of silicone hardness
Silicone is an elastic material whose hardness is typically measured using a Shore A durometer. The Shore A hardness tester is a common mechanical testing instrument used to measure the hardness of elastic materials. During the test, the hardness tester presses a steel bullet into the surface of the object being tested, and calculates the hardness value based on the resistance it experiences. The larger the hardness value, the higher the hardness of the material, and vice versa.

2. Conventional silicone hardness range
The hardness of conventional silicone is usually between 10A-70A, with 10A being the softest type of silicone and 70A being the hardest type. Silicone has a wide range of hardnesses and can be customized based on product needs and usage environments.

3. The impact of silica gel hardness on product performance
The hardness of silicone has a great impact on product performance. Silicone with different hardnesses has different application ranges and properties. Generally speaking, silicone with lower hardness has better softness and flexibility and can be used in products that require high flexibility, such as rubber seals, silicone protective covers, etc. Silicone with higher hardness has better strength and wear resistance, and is suitable for products that require high wear resistance and strength, such as industrial sealing materials, mobile phone casings, etc.

In general, the choice of silicone hardness should be determined based on the specific usage scenarios and performance requirements of the product. At the same time, the hardness of silicone can also be changed through additives, hardness regulators and other means to meet the needs of different fields and products.